A　novel　coordination　polymer　[(C8H20N)(Ag2I3)　([C8H20N](+)　=　tetraethyl　ammonium　(TEA))　was　synthesized　by　the　reaction　of　AgI　and　C8H20NI　at　room　temperature　with　pH　=　6.5,　and　structurally　characterized　by　means　of　X-ray　single-crystal　diffraction.　It　crystallizes　in　orthorhombic,　space　group　Pna2(1)　with　a　=　7.3323(9),　b　=　18.250(2),　c　=　12.5294(15)　A,　C6.33H16.16NAg2I3,　M-r　=　702.76,　V　=　1676.6(4)　angstrom(3),　Z　=　4,　D-c　=　2.784　g/cm(3),　F(000)　=　1256.6,　mu(MoK　alpha)　=　7.828　mm(-1),　the　final　R　=　0.0529　and　wR　=　0.1586　for　1189　observed　reflections　with　I　＞　2　sigma(I).　X-ray　analysis　shows　that　the　[Ag2I3](n)(-)　chain　is　built　up　by　AgI4　tetrahedron　and　in　combination　with　quaternary　ammonium　cations　([C8H20N](+))　by　static　attractive　forces　to　form　the　so-called　organic-inorganic　hybrid　material.