Refined　natural　pyrophyllite　has　been　used　as　a　starting　material　with　other　compouds　for　peparing　sodium　fast　ionic　conductors　Na1+3x+yAlxNdy　Ti2-x-ySi2xPa3-2xO12　by　high　temperature　(900-1100°C)　solid　phase　reaction　for　about　15h.　Nasicon-like　structure　(space　group　R3¯C)　phase　exists　in　the　composition　range　of　y　=　0.3,　x&le0.3;　y　=　0.5,　x&le0.2.　This　phase　possesses　high　ionic　conductivity　at　room　temperature.　The　maximum　conductivity　in　the　above　range　is　the　initial　composition　with　x　=　0.1,　y　=　0.3,　Its　conductivity　is　1.80　×　10-2　S/cm　at　350°.