Sodium　terbium　tungstate　(NaTb(WO4)(2))　single　crystal　with　dimension　empty　set　25　mm　x　30　mm.　and　a　good　optical　quality　was　grown　by　Czochralski　method.　The　transmission　spectrum　was　measured　in　the　visible　and　near-infrared　region　at　room　temperature.　The　specific　Faraday　rotation　of　single　crystal　was　measured　at　room　temperature　in　532,　633,　and　1064　nm　wavelength.　The　Verdet　constant　and　magneto-optical　figure　of　merit　was　investigated.　Comparing　to　the　magneto-optical　figure　of　merit　and　Verdet　constant　for　TGG,　the　NaTb(WO4)(2)　have　larger　magneto-optical　figure　of　merit　and　larger　Verdet　constant.　It　indicates　that　NaTb(WO4)(2)　crystal　can　be　a　promising　magneto-optical　material　in　visible　region.　(C)　2008　Elsevier　B.V.　All　rights　reserved.