Two　novel　transition　metal　phosphonate　compounds,　[Co(H2BDPP)(phen)](n)　1　(BDPP　=　p-O3PCH2(C6H4)CH2PO3,　phen　=　1,10-phenanthroline)　and　[Pb-3(BCP)(2)](n)　2　(BCP　=　OOC(C6H4)CH2PO3),　have　been　synthesized　and　structurally　determined　by　X-ray　single-crystal　diffraction.　Compound　1　crystallizes　in　the　monoclinic　system,　space　group　C2/c　with　a　=　21.169(4),　b　=　12.001(2),　c　=　7.6211(15)　angstrom,　beta　=　98.03(3)degrees,　V　=　1917.2(6)　angstrom(3),　C20H18N2O6P2Co,　M-r　=　505.22,　Z　=　8,　D-c　=　1.737　g/cm(3),　mu　=　1.107　mm(-1),　F(000)　=　1020,　the　final　R　=　0.0450　and　wR　=　0.1306　for　2072　observed　reflections　(I　＞　2　sigma(I)).　Compound　2　crystallizes　in　the　monoclinic　system,　space　group　C2/c　with　a　=　4.7167(9),　b　=　18.753(2),　c　=　22.781(3)　angstrom,　beta　=　91.07(3)degrees,　V　=　2014.7(14)　angstrom(3),　C8H6O5PPb1.5,　M-r　=　523.88,　Z　=　8,　D-c　=　3.454　g/cm(3),　mu　=　25.222　mm(-1),　F(000)　=　1856,　the　final　R　=　0.0441　and　wR　=　0.1906　for　2259　observed　reflections　(I　＞　2　sigma(I)).　In　compound　1,　the　1D　chain　running　along　the　c　axis　is　bridged　by　four　ligands　(trans-HO3PCH2C6H4CH2PO3H)　in　four　different　directions　to　extend　the　structure　into　a　three-dimensional　network.　In　compound　2,　the　Pb(II)　displays　4-　and　5-coordination　modes.　There　is　a　one-dimensional　P-O-Pb　band　along　the　a　axis　formed　by　PO3　groups　and　Pb(II)　cations.　These　bands　are　joined　by　mu(2)-O　of　-COO　to　yield　two-dimensional　inorganic　P-O-Pb　layers　which　are　pillared　by　the　OOCC6H4CH2PO3　ligands　to　form　a　three-dimensional　network.　Moreover,　compound　2　displays　a　strong　emission　band　attributed　to　the　ligand-centered　(LC)　transition.