Nanostructured　porous　MnO2　film　on　Ni　foam　substrate　was　fabricated　via　a　CV　electrodeposited　route　for　the　first　time.　The　obtained　MnO2　film　had　a　3D　network　structure　and　a　high　mass　loading　from　6　to　18　mg　cm(-2).　This　material　achieved　a　maximum　specific　capacitance　of　2790　mF　cm(-2)　at　2　mA　cm(-2)　and　864　mF　cm(-2)　at　20　mA　cm(-2),　and　the　specific　capacitance　can　be　retained　above　90%　after　1000　cycles　at　5　mA　cm(-2).　The　fabricated　AC//MnO2　asymmetric　supercapacitor　can　reach　a　specific　capacitance　of　67　F　g(-1)　and　an　energy　density　of　37.22　Wh　Kg(-1)　with　its　capacitance　retention　of　80%　after　1000　cycles　at　2.5　mA　cm(-2).　(C)　2014　Elsevier　Ltd.　All　rights　reserved.