A　layer　structured　K-doped　(NH4)(2)V3O8/graphene　(K-NVG)　was　prepared　via　a　hydrothermal　route　and　then　used　as　an　anode　material　for　sodium-ion　batteries　for　the　first　time.　The　K-NVG　nanosheets　have　a　diameter　in　the　range　of　200-500　nm.　The　K-NVG　electrode　exhibited　stable　cycling　and　a　good　rate　performance　with　a　reversible　capacity　of　235.4　mA　h　g(-1),　which　is　much　higher　than　the　90.5　mA　h　g(-1)　value　of　the　(NH4)(2)V3O8/graphene　electrode　after　100　cycles　at　a　current　density　of　100　mA　g(-1).　Simultaneously,　the　retention　rate　was　maintained　at　82%　even　after　250　cycles　at　the　current　density　of　300　mA　g(-1).　Such　good　electrochemical　properties　may　be　attributed　to　the　K-NVG＇s　stable　layered　structure.