A　new　complex,　Co0.5Ni0.5(C2H6N2O)(6)SO4　(I),　was　synthesized　and　its　single　crystalwas　obtained　from　aqueous　solution　by　evaporating　solvent　slowly.　Single-crystal　X-ray　analysis　revealed　that　the　complex　belongs　to　trigonal　system,　space　group　R-3c,　with　a　=　b　=　10.999(2)　angstrom,　c　=　40.439(13)　angstrom,　V　=　4237(2)　angstrom(3),　Z　=　6,　D-c　=　1.410　g/cm(3),　Mr　=　599.41,　mu　=　0.785　mm(-1),　F(000)　=　1893,　the　final　R　=　0.0330　and　wR　=　0.0926　(I　＞　2　sigma(I)).　IR　spectrum　and　compositional　analyses　(elemental　analyzer　and　ICP)　were　used　to　characterize　the　composition　of　the　product.　TGA　(Thermal　Gravimetric　Analysis)　showed　that　complex　I　remained　stable　until　it　is　heated　up　to　200.,　indicating　its　good　thermostability.　The　main　transmission　peak　of　complex　I　in　UV-Vis　spectrum　appeared　at　290　nm,　making　it　an　eligible　material　for　ultraviolet　light　filters　(ULF).