In　this　work,　hierarchically　mesoporous　TiO2　spheres　were　successfully　fabricated.　The　synthesis　method　could　be　simply　described　as　adding　Ti(SO4)(2)　into　the　disperse　phase　of　a　conventional　emulsion　polymerization　where　emulgator　was　discovered　to　play　an　important　role　in　the　formation　of　the　ingenious　structure.　When　used　as　anode　materials　for　lithium-ion　batteries,　it　delivered　a　high　capacity　of　192　mA　h　g(-1)　at　0.2　A　g(-1)　with　the　retention　of　94.3%　after　100　cycles,　and　a　reversible　capacity　of　114　mA　h　g(-1)　could　be　kept　at　2　A　g(-1)　after　2000　cycles.　At　the　same　time,　an　excellent　initial　Coulombic　efficiency　(＞　90%)　and　satisfactory　rate　performance　were　obtained.