Two　series　of　Dy3+:NaTb(WO4)2　and　Dy3+:NaGd(WO4)2　phosphors　doped　with　different　Dy3+　concentrations　were　prepared　by　the　solid-state　reaction　method.　Dy3+→Tb3+　energy　transfer　and　fluorescence　properties　of　Dy3+:NaTb(WO4)2　phosphors　doped　with　different　Dy3+　concentrations　were　firstly　investigated　by　exciting　at　455　nm.　Strong　Tb3+　green　fluorescence　around　545　nm　was　observed　in　the　Dy3+:NaTb(WO4)2　phosphors　due　to　the　efficient　Dy3+→Tb3+　energy　transfer.　Excited　at　455　nm,　polarized　spectroscopic　properties　of　a　(9.28　at.%)Dy3+:NaTb(WO4)2　crystal　grown　by　the　Czochralski　method　were　studied　at　room　temperature.　The　peak　absorption　cross-sections　of　the　crystal　at　454.6　nm,　corresponding　to　the　6H15/2　→　4I15/2　transition　of　Dy3+,　are　2.74　×　10−21　and　3.93　×　10−21　cm2　for　σ　and　π　polarizations,　respectively.　The　peak　emission　cross-sections　of　the　crystal,　corresponding　to　the　5D4→7F5　transition　of　Tb3+,　are　5.6　×　10−21　at　545　nm　and　11.5　×　10−21　cm2　at　548.6　nm　for　σ　and　π　polarizations,　respectively.　Tb3+　green　fluorescence　around　545　nm　was　obviously　enhanced　in　the　crystal　excited　at　455　nm　due　to　the　Dy3+→Tb3+　energy　transfer.　The　results　show　that　Dy3+　can　be　used　as　sensitizing　ions　to　enhance　the　visible　fluorescence　of　Tb3+　in　the　NaTb(WO4)2　phosphor　and　crystal　excited　at　455　nm.　©　2023　Elsevier　B.V.