Cu　nanowires　and　a　nanoporous　Ag　matrix　were　fabricated　through　directional　solidification　and　selective　dissolution　of　Ag–Cu　eutectic　alloys.　Ag-39.9at.%Cu　eutectic　alloys　were　directionally　solidified　at　growth　rates　of　14,　25,　and　34　μm/s　at　a　temperature　gradient　of　10　K/cm.　The　Cu　phase　in　the　Ag　matrix　gradually　changed　from　lamellar　to　fibrous　with　an　increase　in　the　growth　rate.　The　Ag　matrix　phase　was　selectively　dissolved,　and　Cu　nanowires　of　300–600　nm　in　diameter　and　tens　of　microns　in　length　were　prepared　in　0.1　M　borate　buffer　with　a　pH　of　9.18　at　a　constant　potential　of　0.7　V　(vs.　SCE).　The　nanoporous　Ag　matrix　was　fabricated　through　selective　dissolution　of　Cu　fiber　phase　in　0.1　M　acetate　buffer　with　a　pH　of　6.0　at　a　constant　potential　of　0.5　V　(vs.　SCE).　The　diameter　of　Ag　pores　decreased　with　increasing　growth　rate.　The　diameter　and　depth　of　Ag　pores　increased　when　corrosion　time　was　extended.　The　depth　of　the　pores　was　30　μm　after　12　h.　©　2022　by　the　authors.