After　exposure　to　oxygen-poor　(10(-13　)-10(-14)　wt%)　liquid　lead-bismuth　eutectic　(LBE)　at　500　degrees　C　for　500　h,　LBE　penetrates　more　than　one　order　of　magnitude　deeper　in　an　FCC　Al0.4CoCrFeNi　high-entropy　alloy　(HEA)　decorated　with　a　network　of　BCC　(Ni,　Al)-rich　intergranular　(IG)　precipitates　than　in　a　single-phase,　FCC　Al0.3CoCrFeNi　HEA　without　the　IG　precipitate　network.　This　deterioration　of　corrosion　resistance　is　attributed　to　the　energetic　nature　of　the　BCC/FCC　interphase　boundaries　(IBs)　and　resultant　IB　wetting.　The　LBE　ingress　film　selectively　leaches　nickel　located　at　those　low-indexed　crystalline　planes,　resulting　in　phase　transformation　from　FCC　to　BCC　structure.