This　paper　presents　an　experimental　investigation　on　the　mechanical　properties　of　sandwich　tempered　glass　unidirectional　composite　laminate　under　uniformly　distributed　load.　A　total　of　sixty-four　specimens　are　tested　to　investigate　the　influence　of　individual　layer　thickness　of　tempered　glass　panel　(T),　bearing　length　(BL),　and　length　of　loading　end　(LLE).　According　to　this　experiment,　the　failure　modes　of　tested　specimens　were　observed　in　detail　during　load　procedure.　The　effects　of　the　three　variables　on　the　ultimate　bearing　capacity,　stiffness　and　stress　distribution　of　sandwich　tempered　glass　unidirectional　composite　laminate　are　discussed.　The　results　indicate　that　the　three　variables　have　positive　effect　on　bearing　capacity　and　secant　stiffness　of　the　sandwich　tempered　glass　unidirectional　composite　laminate.　And　the　individual　layer　thickness　of　tempered　glass　panel　has　the　greatest　influence　on　the　ultimate　bearing　capacity　and　secant　stiffness　of　specimens.　With　increasing　of　thickness,　bearing　length　and　length　of　loading　end,　the　bearing　capacity　and　the　stiffness　are　increased.　Based　on　the　results　of　parametric　studies,　the　designed　formulas　are　proposed　to　estimate　the　ultimate　bearing　capacity　of　sandwich　tempered　glass　unidirectional　composite　laminate　under　local　uniformly　distributed　load.