Ca　1-3xLn　2xTiO　3　(Ln=La,　Nd,　Sm;　x=0.13,　0.20)　ceramics　were　investigated　systematically　to　dicuss　the　influences　of　sintering　temperature,　compositions,　Ln　3+　ions　on　its　sintering　property,　crystal　structure　and　microstructure.　The　results　show　that　the　dense　ceramics　were　obtained　in　the　sintering　temperature　range　of　1300∼1350　°C　and　the　relative　density　reached　over　97%.　Sintering　temperature　was　50∼150　°C　lower　than　previous　reports.　Single　orthogonal　perovskite　structure　phase　was　formed　except　that　a　little　secondary　phase　Sm　2Ti　2O　7　was　detected　by　XRD　analysis　when　x=0.20　and　Ln=Sm.　The　growth　pattern　of　Ca　1-3xLn　2xTiO　3　grains　was　terracing　growth.　©　(2012)　Trans　Tech　Publications.