A　new　three-matrix　mixed　vanadate　crystal　Nd:Lu　0.33Y　0.36Gd　0.3VO　4　(Nd:LuYGdVO　4)　crystal　was　grown　by　the　Czochralski　method.　Room　temperature　absorption　and　fluorescence　spectra　of　the　Nd:LuYGdVO　4　crystals　were　measured　and　the　spectroscopic　parameters　were　calculated　by　the　Judd-Ofelt　theory.　The　intensity　parameters　of　the　Nd:LuYGdVO　4　crystal　were　Ω　2　=　9.736　×　10　-20　cm　2,　Ω　4　=　4.179　×　10　-20　cm　2,　Ω　6　=　8.020　×　10　-20　cm　2　and　the　stimulate　emission　cross　section　was　5.3　×　10　-19　cm　2.　Diode-pumped　actively　Q-switched　and　passively　Q-switched　Nd:LuYGdVO　4　and　Nd:Lu　0.14Y　0.86VO4　lasers　at　1.06　μm　were　demonstrated.　The　results　indicate　that,　for　both　actively　and　passively　Q-switched　lasers,　the　Nd:LuYGdVO　4　lasers　can　generate　shorter　pulse　width　with　higher　peak　power　than　the　Nd:Lu　0.14Y　0.86VO　4　lasers　at　the　same　cavity　conditions.　©　Pleiades　Publishing,　Ltd.,　2012.