Thin-film　encapsulation　(TFE)　is　essential　and　challenging　for　flexible　organic/quantum　dot　light-emitting　diodes　(OLEDs/QLEDs).　In　this　work,　SiO2　nanoparticles　were　added　into　the　NEA　121　polymer　(s-NEA)　to　prolong　the　permeation　pathways,　showing　good　barrier　property　and　high　optical　transparency.　With　increasing　the　concentration　of　SiO2　nanoparticles　up　to　20 mg/ml,　the　value　of　water　vapor　transmission　rate　(WVTR)　decreased.　A　single　s-NEA　layer　with　silica　concentration　of　20 mg/ml　and　thickness　of　~　75 µm　exhibited　WVTR　of　2.5　×　10−3 g/m2/day　and　light　transmittance　of　above　80%.　Al2O3　thin　films　fabricated　using　atomic　layer　deposition　were　inserted　between　s-NEA　layers　to　form　dyad-style　Al2O3/s-NEA　multilayers.　The　Al2O3　(60 nm)/s-NEA　(20 µm)　multilayers　with　3　units　exhibited　WVTR　of　2.6　×　10−5 g/m2/day　and　consistently　demonstrated　a　significantly　extended　QLED　lifetime.　©　2019,　Springer　Science+Business　Media,　LLC,　part　of　Springer　Nature.