Transparent　bulk　glass　ceramics　of　4.5ZnO-5.5Al2O3-90SiO2　(ZAS)　and　single　doped　ZAS:RE3+　(RE=Eu,　Tb,　Ce)　were　synthesized　by　sol-gel　method.　X-ray　diffraction　(XRD),　transmission　electron　microscopy　(TEM)　and　photoluminescence　(PL)　spectra　were　employed　to　study　the　influence　of　doping　rare-earth　ions　concentration　on　the　structure　and　luminescence　properties　of　ZAS　glass-ceramics.　XRD　results　show　that　ZAS:RE3+　(RE=Eu,　Tb,　Ce)　glass　ceramics　heat-treated　at　900　consist　of　ZnAl2O4　phase　with　average　grain　size　of　30　nm　and　amorphous　SiO2.TEM　results　show　that　ZnAl2O4　were　precipitated　from　ZAS　system　when　heat-treated　at　900　,　and　doping　ions　have　not　changed　the　original　structure.　PL　spectra　indicate　that　ZAS:Eu3+　emits　intense　611　nm　red　light　originating　from　5D0→7F2　transition　of　Eu3+　ions,　ZAS:Tb3+　shows　541　nm　green　emission　attributed　to　5D4→7F5　transition　of　Tb3+　ions,　and　ZAS:Ce3+　gives　381　nm　blue　light　corresponding　to　the　5d　to　4f　transition　of　Ce3+　ions.　Furthermore,　the　concentration　quenching　phenomena　are　observed　while　the　single　doping　mole　fraction　of　Eu3+,　Tb3+　and　Ce3+　was　20%,　20%　and　3%,　respectively.　The　excellent　Commission　International　de　I＇Eclairage　(CIE)　chromaticity　coordinates　of　ZAS:RE3+　(RE=Eu,　Tb,　Ce)　glass-ceramics　indicate　that　they　are　good　candidates　for　the　application　of　white　LEDs.　©,　2015,　Chines　Academy　of　Sciences.　All　right　reserved.