The　3003　Al　alloy　was　deformed　by　isothermal　compression　in　the　range　of　deformation　temperature　300-500　degrees　C　at　strain　rate　0.01-10.0　s(-1)　with　Gleeble-1500　thermal　simulator.　Processing　maps　at　a　strain　of　0.6　for　hot　working　were　developed　on　a　dynamic　materials　model.　The　maps　exhibit　a　flow　instability　domain　at　about　300　degrees　C-380　degrees　C　and　1.0-10.0　s(-1)　DRX　occurs　extensively　in　the　temperature　range　of　450-500　degrees　C　and　at　the　strain　rate　of　10.0　s(-1).　The　optimum　parameters　of　hot　working　for　3003　Al　alloy　at　the　strain　of　0.6　are　confined　at　500　degrees　C　and　10.0　s(-1)　with　the　highest　efficiency　(37%).