Texture　characteristics　of　the　1235　aluminum　alloy　at　different　rolling-deformation　levels　were　studied　with　EBSD.　The　effects　of　hot　rolling,　cold　rolling　and　plastic　deformation　on　the　ODF　and　texture　components　of　the　material　were　studied　as　well.　The　main　textures　of　the　hot-rolled　material　were　the　cube　texture　and　the　R　texture.　The　greater　was　the　deformation　of　the　material,　the　stronger　was　the　texture.　The　recrystallization　texture　of　the　90-%　hot-rolled　alloy　was　stronger　than　that　of　the　material　after　50-%　hot　rolling.　The　R　texture　was　the　main　texture　of　the　50-%　hot-rolled　material,　but　it　changed　into　the　cube　texture　after　90-%　hot　rolling.　Recrystallization　was　obvious　during　hot　rolling.　The　90-%　cold-rolled　material　showed　typical　copper-texture　characteristics,　and　work　hardening　was　notable.